Radilon? D 40P50K 100 NAT 5526
聚酰胺610
PA610 flexible, high viscosity extrusion grade. Plasticized. Heat stabilized. Natural colour.
Suitable for extrusion of tubes and profiles. Typical application: air pressure pipes.
This grade is partially renewably-sourced (60% of base polymer by weight).
添加劑 | |
特性 | - 經(jīng)增塑、可更新資源、熱穩(wěn)定性、粘度高
|
用途 | |
RoHS 合規(guī)性 | |
外觀 | |
加工方法 | |
樹(shù)脂ID (ISO 1043) | |
密度 | 1.10 | -- | g/cm3 | ISO 1183 |
吸水率 |
|
|
| ISO 62 |
飽和, 73°F, 0.0787 in | 2.5 | -- | % |
|
平衡, 73°F, 0.0787 in, 50% RH | 1.1 | -- | % |
|
拉伸模量 | 125000 | 79800 | psi | ISO 527-2/1A/1 |
拉伸應(yīng)力 |
|
|
|
|
屈服 | 5800 | 4350 | psi | ISO 527-2/1A/50 |
斷裂 | 7690 | -- | psi | ISO 527-2/1A/5 |
拉伸應(yīng)變 (屈服) | 55 | -- | % | ISO 527-2/1A/50 |
標(biāo)稱拉伸斷裂應(yīng)變 | 300 | > 100 | % | ISO 527-2/1A/50 |
彎曲模量 2 | 97200 | -- | psi | ISO 178 |
彎曲應(yīng)力 2 | 4350 | -- | psi | ISO 178 |
簡(jiǎn)支梁缺口沖擊強(qiáng)度 |
|
|
| ISO 179/1eA |
-22°F | 2.9 | -- | ft·lb/in2 |
|
73°F | 9.5 | 17 | ft·lb/in2 |
|
熱變形溫度 (264 psi, 未退火) | 122 | -- | °F | ISO 75-2/Af |
熔融溫度 3 | 419 | -- | °F | ISO 11357-3 |
表面電阻率 4 | 1.0E+12 | -- | ohms | IEC 60093 |
體積電阻率 4 | 1.0E+15 | -- | ohms·cm | IEC 60093 |
干燥溫度 - 熱風(fēng)干燥機(jī) | 176 | °F |
|
干燥時(shí)間 - 熱風(fēng)干燥機(jī) | 2.0 到 4.0 | hr |
|
Dew Point - 熱風(fēng)干燥機(jī) | -4 | °F |
|
建議的最大水分含量 | 0.10 | % |
|
加工（熔體）溫度 | 446 到 500 | °F |
|
模具溫度 | 158 到 176 | °F |
|
注射速度 | 中等 |
|
|
熔體溫度 | 446 到 482 | °F |
|