CYCOLOY? FR Resin CY6310
聚碳酸酯+丙烯腈丁二烯苯乙烯
產(chǎn)品說(shuō)明:
CYCOLOY CY6310 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is a hydrolytically stable, impact modified grade that can be injection molded. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 & 5VA/B flame rating. CYCOLOY CY6310 resin is an excellent candidate for a wide variety of large size of applications including appliances, lighting, electrical and enclosures.
添加劑 | |
特性 | - Chlorine Free，水解穩(wěn)定，無(wú)溴，阻燃性
|
用途 | - Lighting Applications，電氣/電子應(yīng)用領(lǐng)域，電器用具，建筑應(yīng)用領(lǐng)域
|
加工方法 | |
Also Available In | |
密度 / 比重 |
|
|
|
-- | 1.17 |
| ASTM D792 |
-- | 1.17 | g/cm3 | ISO 1183 |
熔流率（熔體流動(dòng)速率） |
|
| ASTM D1238 |
250°C/2.16 kg | 16 | g/10 min |
|
260°C/2.16 kg | 20 | g/10 min |
|
熔融體積流量（MVR） (260°C/2.16 kg) | 1.16 | in3/10min | ISO 1133 |
收縮率 - 流動(dòng) (0.126 in) | 4.0E-3 到 6.0E-3 | in/in | 內(nèi)部方法 |
吸水率 |
|
| ISO 62 |
飽和, 73°F | 0.60 | % |
|
平衡, 73°F, 50% RH | 0.20 | % |
|
拉伸模量 |
|
|
|
-- 2 | 392000 | psi | ASTM D638 |
-- | 392000 | psi | ISO 527-2/1 |
抗張強(qiáng)度 |
|
|
|
屈服 3 | 9140 | psi | ASTM D638 |
屈服 | 9140 | psi | ISO 527-2/50 |
斷裂 3 | 7250 | psi | ASTM D638 |
斷裂 | 7400 | psi | ISO 527-2/50 |
伸長(zhǎng)率 |
|
|
|
屈服 3 | 4.2 | % | ASTM D638 |
屈服 | 4.4 | % | ISO 527-2/50 |
斷裂 3 | > 50 | % | ASTM D638 |
斷裂 | > 50 | % | ISO 527-2/50 |
彎曲模量 |
|
|
|
1.97 in 跨距 4 | 392000 | psi | ASTM D790 |
-- 5 | 384000 | psi | ISO 178 |
彎曲應(yīng)力 |
|
|
|
-- 5, 6 | 13200 | psi | ISO 178 |
屈服, 1.97 in 跨距 4 | 14600 | psi | ASTM D790 |
簡(jiǎn)支梁缺口沖擊強(qiáng)度 7 |
|
| ISO 179/1eA |
-22°F | 6.7 | ft·lb/in2 |
|
73°F | 26 | ft·lb/in2 |
|
簡(jiǎn)支梁無(wú)缺口沖擊強(qiáng)度 7 (73°F) | 無(wú)斷裂 |
| ISO 179/1eU |
懸壁梁缺口沖擊強(qiáng)度 |
|
|
|
-22°F | 2.2 | ft·lb/in | ASTM D256 |
73°F | 11 | ft·lb/in | ASTM D256 |
-22°F 8 | 6.2 | ft·lb/in2 | ISO 180/1A |
73°F 8 | 24 | ft·lb/in2 | ISO 180/1A |
無(wú)缺口伊佐德沖擊強(qiáng)度 8 (73°F) | 無(wú)斷裂 |
| ISO 180/1U |
裝有測(cè)量?jī)x表的落鏢沖擊 |
|
|
|
73°F, Total Energy | 575 | in·lb | ASTM D3763 |
-- | 77.4 | ft·lb | ISO 6603-2 |
載荷下熱變形溫度 |
|
|
|
66 psi, 未退火, 0.126 in | 212 | °F | ASTM D648 |
264 psi, 未退火, 0.126 in | 190 | °F | ASTM D648 |
264 psi, 未退火, 0.157 in, 2.52 in 跨距 9 | 194 | °F | ISO 75-2/Af |
維卡軟化溫度 |
|
|
|
-- | 228 | °F | ASTM D1525 10, ISO 306/B50 10 |
-- | 232 | °F | ISO 306/B120 |
Ball Pressure Test |
|
| IEC 60695-10-2 |
163 到 171°F | 通過(guò) |
|
|
203°F 11 | 通過(guò) |
|
|
線形熱膨脹系數(shù) |
|
|
|
流動(dòng) : -40 到 104°F | 3.8E-5 | in/in/°F | ASTM E831, ISO 11359-2 |
橫向 : -40 到 104°F | 3.9E-5 | in/in/°F | ASTM E831 |
橫向 : -40°F | 3.9E-5 | in/in/°F | ISO 11359-2 |
RTI Elec | 185 | °F | UL 746 |
RTI Imp | 185 | °F | UL 746 |
RTI | 185 | °F | UL 746 |
表面電阻率 | > 1.0E+15 | ohms | IEC 60093 |
體積電阻率 | > 1.0E+15 | ohms·cm | IEC 60093 |
漏電起痕指數(shù) | 575 | V | IEC 60112 |
高電弧燃燒指數(shù)(HAI) 12 | PLC 0 |
| UL 746 |
熱絲引燃 (HWI) | PLC 3 |
| UL 746 |
UL 阻燃等級(jí) |
|
| UL 94 |
0.030 in | V-2 |
|
|
0.030 in, Testing by SABIC | V-2 |
|
|
0.06 in | V-0 |
|
|
0.06 in, Testing by SABIC | V-0 |
|
|
0.09 in | 5VB |
|
|
0.09 in, Testing by SABIC | 5VB |
|
|
0.11 in | 5VA |
|
|
0.11 in, Testing by SABIC | 5VA |
|
|
灼熱絲易燃指數(shù) (0.12 in) | 1760 | °F | IEC 60695-2-12 |
極限氧指數(shù) | 30 | % | ISO 4589-2 |
干燥溫度 | 194 到 212 | °F |
|
干燥時(shí)間 | 2.0 到 4.0 | hr |
|
建議的最大水分含量 | 0.020 | % |
|
料斗溫度 | 140 到 176 | °F |
|
料筒后部溫度 | 410 到 464 | °F |
|
料筒中部溫度 | 446 到 518 | °F |
|
料筒前部溫度 | 464 到 536 | °F |
|
射嘴溫度 | 446 到 518 | °F |
|
加工（熔體）溫度 | 482 到 536 | °F |
|
模具溫度 | 140 到 194 | °F |
|