CYCOLOY? Resin C1200HF
聚碳酸酯+丙烯腈丁二烯苯乙烯
產(chǎn)品說明:
PC+ABS, excellent flow/impact/high heat resistance. Low temperature ductility.
特性 | |
加工方法 | |
多點數(shù)據(jù) | Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Elastic Modulus vs Temperature (ASTM D4065) Flexural DMA (ASTM D4065) Instrumented Impact (Energy) (ASTM D3763) Instrumented Impact (Load) (ASTM D3763) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835)
|
密度 / 比重 | 1.15 |
| ASTM D792 |
熔流率（熔體流動速率） (260°C/5.0 kg) | 19 | g/10 min | ASTM D1238 |
熔融體積流量（MVR） (265°C/5.0 kg) | 1.46 | in3/10min | ISO 1133 |
收縮率 - 流動 (0.126 in) | 5.0E-3 到 7.0E-3 | in/in | 內(nèi)部方法 |
拉伸模量 |
|
|
|
-- 3 | 330000 | psi | ASTM D638 |
-- | 344000 | psi | ISO 527-2/1 |
抗張強度 |
|
|
|
屈服 4 | 8300 | psi | ASTM D638 |
屈服 | 7980 | psi | ISO 527-2/50 |
伸長率 |
|
|
|
屈服 4 | 5.0 | % | ASTM D638 |
屈服 | 4.8 | % | ISO 527-2/50 |
斷裂 4 | 150 | % | ASTM D638 |
斷裂 | 110 | % | ISO 527-2/50 |
彎曲模量 |
|
|
|
1.97 in 跨距 5 | 340000 | psi | ASTM D790 |
-- | 327000 | psi | ISO 178 |
彎曲應(yīng)力 |
|
|
|
-- | 12500 | psi | ISO 178 |
屈服, 1.97 in 跨距 5 | 12800 | psi | ASTM D790 |
懸壁梁缺口沖擊強度 |
|
|
|
-22°F | 9.0 | ft·lb/in | ASTM D256 |
73°F | 11 | ft·lb/in | ASTM D256 |
-22°F 6 | 16 | ft·lb/in2 | ISO 180/1A |
73°F 6 | 23 | ft·lb/in2 | ISO 180/1A |
裝有測量儀表的落鏢沖擊 |
|
| ASTM D3763 |
-22°F, Total Energy | 480 | in·lb |
|
73°F, Total Energy | 480 | in·lb |
|
載荷下熱變形溫度 |
|
|
|
66 psi, 未退火, 0.126 in | 265 | °F | ASTM D648 |
66 psi, 未退火, 2.52 in 跨距 7 | 266 | °F | ISO 75-2/Bf |
264 psi, 未退火, 0.126 in | 235 | °F | ASTM D648 |
264 psi, 未退火, 2.52 in 跨距 7 | 230 | °F | ISO 75-2/Af |
維卡軟化溫度 | 266 | °F | ISO 306/B50 |
線形熱膨脹系數(shù) - 流動 (-40 到 104°F) | 4.0E-5 | in/in/°F | ASTM E831 |
RTI Elec | 221 | °F | UL 746 |
RTI Imp | 176 | °F | UL 746 |
RTI | 221 | °F | UL 746 |
相比耐漏電起痕指數(shù)(CTI) | PLC 2 |
| UL 746 |
高電弧燃燒指數(shù)(HAI) | PLC 1 |
| UL 746 |
熱絲引燃 (HWI) | PLC 3 |
| UL 746 |
UL 阻燃等級 (0.05 in) | HB |
| UL 94 |
干燥溫度 | 212 到 230 | °F |
|
干燥時間 | 3.0 到 4.0 | hr |
|
干燥時間，最大 | 8.0 | hr |
|
建議的最大水分含量 | 0.020 | % |
|
建議注射量 | 30 到 80 | % |
|
料斗溫度 | 140 到 176 | °F |
|
料筒后部溫度 | 482 到 554 | °F |
|
料筒中部溫度 | 491 到 563 | °F |
|
料筒前部溫度 | 500 到 572 | °F |
|
射嘴溫度 | 527 到 572 | °F |
|
加工（熔體）溫度 | 527 到 572 | °F |
|
模具溫度 | 140 到 194 | °F |
|
背壓 | 43.5 到 102 | psi |
|
螺桿轉(zhuǎn)速 | 40 到 70 | rpm |
|
排氣孔深度 | 1.5E-3 到 3.0E-3 | in |
|
如需沙伯基礎(chǔ)（SABIC）原廠物性表及相關(guān)文件，請聯(lián)系我們工作人員，謝謝！