RTP VLF 84009
聚二甲苯酰胺
Long Glass Fiber - Heat Stabilized
填料/增強(qiáng)材料 | |
添加劑 | |
特性 | |
RoHS 合規(guī)性 | |
加工方法 | |
密度 / 比重 | 1.65 |
| ASTM D792 |
收縮率 - 流動(dòng) (0.126 in) | 1.0E-3 到 3.0E-3 | in/in | ASTM D955 |
含水量 | 0.050 | % |
|
拉伸模量 | 2.60E+6 | psi | ASTM D638 |
抗張強(qiáng)度 | 39000 | psi | ASTM D638 |
伸長(zhǎng)率 (屈服) | 1.0 到 2.0 | % | ASTM D638 |
彎曲模量 | 2.70E+6 | psi | ASTM D790 |
彎曲強(qiáng)度 | 56000 | psi | ASTM D790 |
懸壁梁缺口沖擊強(qiáng)度 (0.126 in) | 6.5 | ft·lb/in | ASTM D256 |
無(wú)缺口懸臂梁沖擊 (0.126 in) | 20 | ft·lb/in | ASTM D4812 |
載荷下熱變形溫度 (264 psi, 未退火) | 530 | °F | ASTM D648 |
UL 阻燃等級(jí) (0.06 in, ** Values per RTP Company testing.) | HB |
| UL 94 |
干燥溫度 | 250 | °F |
|
干燥時(shí)間 | 4.0 | hr |
|
Dew Point | -25 | °F |
|
加工（熔體）溫度 | 580 到 625 | °F |
|
模具溫度 | 275 到 325 | °F |
|
注塑壓力 | 10000 到 18000 | psi |
|
Use a reverse barrel profile. To maximize fiber length, the following injection barrel, screw, and tip designs should be followed. L/D ratio 16/1 - 22/1, Compression ratio 2:1, Flight depth 0.200 in (5 mm) minimum, in feed section, Screw diameter 0.65 - 0
Desiccant Type Dryer Required. |