Ultrason? S 6010
聚砜
產(chǎn)品說(shuō)明:
Ultrason S 6010 is a high molecular weight injection molding and extrusion grade with excellent chemical resistance (stress crack resistance) and good solubility in typical solvents (N-methylpyrrolidone, dimethlyacetamide, dicholormethane) used in the production of membranes or coatings.
Applications
Typical applications include sanitary and heating systems/parts and membranes.
特性 | |
用途 | |
機(jī)構(gòu)評(píng)級(jí) | |
RoHS 合規(guī)性 | |
形式 | |
加工方法 | |
多點(diǎn)數(shù)據(jù) | |
密度 | 1.23 | g/cm3 | ISO 1183 |
溶化體積流率（MVR） (360°C/10.0 kg) | 1.83 | in3/10min | ISO 1133 |
收縮率 |
|
| ISO 294-4 |
橫向流量 | 0.77 | % |
|
流量 | 0.72 | % |
|
吸水率 |
|
| ISO 62 |
飽和, 73°F | 0.80 | % |
|
平衡, 73°F, 50% RH | 0.30 | % |
|
球壓硬度 | 19600 | psi | ISO 2039-1 |
拉伸模量 (73°F) | 370000 | psi | ISO 527-2 |
拉伸應(yīng)力 (屈服, 73°F) | 10900 | psi | ISO 527-2 |
拉伸應(yīng)變 (屈服, 73°F) | 5.7 | % | ISO 527-2 |
簡(jiǎn)支梁缺口沖擊強(qiáng)度 |
|
| ISO 179 |
-22°F | 3.1 | ft·lb/in2 |
|
73°F | 2.9 | ft·lb/in2 |
|
簡(jiǎn)支梁無(wú)缺口沖擊強(qiáng)度 |
|
| ISO 179 |
-22°F | 無(wú)斷裂 |
|
|
73°F | 無(wú)斷裂 |
|
|
懸壁梁缺口沖擊強(qiáng)度 |
|
| ISO 180 |
-22°F | 3.1 | ft·lb/in2 |
|
73°F | 2.9 | ft·lb/in2 |
|
熱變形溫度 (264 psi, 未退火) | 351 | °F | ISO 75-2/A |
線形熱膨脹系數(shù) - 流動(dòng) | 2.9E-5 | in/in/°F |
|
表面電阻率 | > 1.0E+15 | ohms | IEC 60093 |
體積電阻率 | > 1.0E+15 | ohms·cm | IEC 60093 |
介電強(qiáng)度 | 940 | V/mil | IEC 60243-1 |
介電常數(shù) |
|
| IEC 60250 |
100 Hz | 3.50 |
|
|
1 MHz | 3.40 |
|
|
耗散因數(shù) |
|
| IEC 60250 |
100 Hz | 1.1E-3 |
|
|
1 MHz | 7.1E-3 |
|
|
漏電起痕指數(shù) | 125 | V | IEC 60112 |
干燥溫度 | 266 到 302 | °F |
|
干燥時(shí)間 | 4.0 | hr |
|
建議的最大水分含量 | 0.020 | % |
|
加工（熔體）溫度 | 644 到 734 | °F |
|
模具溫度 | 284 到 356 | °F |
|
注塑壓力 | 508 到 1810 | psi |
|
注射速度 | 快速 |
|
|