Ultraform? S 2320 003 UNC Q600
聚甲醛（POM）共聚物
產(chǎn)品說明:
Ultraform S 2320 003 UNC Q600 is an easy flowing and rapidly freezing injection molding POM grade. Contains a mold release agent.
Applications
Typical applications include difficult, thin-walled parts.
添加劑 | |
特性 | |
用途 | |
機(jī)構(gòu)評(píng)級(jí) | |
RoHS 合規(guī)性 | |
形式 | |
加工方法 | |
多點(diǎn)數(shù)據(jù) | Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Specific Heat vs. Temperature (ISO 11403-2) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)
|
密度 / 比重 |
|
|
|
-- | 1.40 |
| ASTM D792 |
-- | 1.40 | g/cm3 | ISO 1183 |
溶化體積流率（MVR） (190°C/2.16 kg) | 0.671 | in3/10min | ISO 1133 |
收縮率 |
|
|
|
流動(dòng) : 0.125 in | 0.020 | in/in |
|
橫向流量 | 2.1 | % | ISO 294-4 |
流量 | 2.1 | % | ISO 294-4 |
吸水率 |
|
|
|
飽和 | 0.80 | % | ASTM D570 |
飽和, 73°F | 0.80 | % | ISO 62 |
平衡, 50% RH | 0.20 | % | ASTM D570 |
平衡, 73°F, 50% RH | 0.20 | % | ISO 62 |
拉伸模量 (73°F) | 392000 | psi | ISO 527-2 |
抗張強(qiáng)度 |
|
|
|
屈服, 73°F | 9430 | psi | ASTM D638, ISO 527-2 |
屈服, -40°F | 13500 | psi | ISO 527-2 |
屈服, 176°F | 4790 | psi | ISO 527-2 |
伸長(zhǎng)率 (屈服, 73°F) | 9.0 | % | ASTM D638, ISO 527-2 |
標(biāo)稱拉伸斷裂應(yīng)變 (73°F) | 28 | % | ISO 527-2 |
拉伸蠕變模量 |
|
| ISO 899-1 |
1 hr | 276000 | psi |
|
1000 hr | 189000 | psi |
|
彎曲模量 (73°F) | 380000 | psi | ASTM D790 |
簡(jiǎn)支梁缺口沖擊強(qiáng)度 |
|
| ISO 179 |
-22°F | 2.4 | ft·lb/in2 |
|
73°F | 2.6 | ft·lb/in2 |
|
簡(jiǎn)支梁無缺口沖擊強(qiáng)度 |
|
| ISO 179 |
-22°F | 81 | ft·lb/in2 |
|
73°F | 86 | ft·lb/in2 |
|
懸壁梁缺口沖擊強(qiáng)度 |
|
| ASTM D256 |
-40°F | 0.94 | ft·lb/in |
|
73°F | 1.1 | ft·lb/in |
|
載荷下熱變形溫度 |
|
|
|
66 psi, 未退火 | 320 | °F | ASTM D648 |
66 psi, 未退火 | 313 | °F | ISO 75-2/B |
264 psi, 未退火 | 230 | °F | ASTM D648 |
264 psi, 未退火 | 212 | °F | ISO 75-2/A |
熔融峰值溫度 | 333 | °F | ASTM D3418, ISO 3146 |
線形熱膨脹系數(shù) - 流動(dòng) |
|
|
|
-- | 3.3E-5 | in/in/°F | ASTM E831 |
-- | 6.1E-5 | in/in/°F |
|
表面電阻率 |
|
|
|
0.0591 in | 1.0E+13 | ohms | ASTM D257 |
-- | 1.0E+13 | ohms | IEC 60093 |
體積電阻率 |
|
|
|
0.0591 in | 1.0E+15 | ohms·cm | ASTM D257 |
-- | 1.0E+15 | ohms·cm | IEC 60093 |
介電強(qiáng)度 | 1000 | V/mil | IEC 60243-1 |
介電常數(shù) |
|
| IEC 60250 |
100 Hz | 3.80 |
|
|
1 MHz | 3.80 |
|
|
耗散因數(shù) |
|
| IEC 60250 |
100 Hz | 1.0E-3 |
|
|
1 MHz | 5.0E-3 |
|
|
漏電起痕指數(shù) | 600 | V | IEC 60112 |
干燥溫度 | 176 到 230 | °F |
|
干燥時(shí)間 | 2.0 到 4.0 | hr |
|
建議的最大水分含量 | 0.15 | % |
|
加工（熔體）溫度 | 374 到 446 | °F |
|
模具溫度 | 140 到 248 | °F |
|
注塑壓力 | 508 到 1020 | psi |
|
如需巴斯夫原廠物性表及相關(guān)文件，請(qǐng)聯(lián)系我們工作人員，謝謝！