Ultradur? S 4090 G2
聚對(duì)苯二甲酸丁二酯 + ASA
產(chǎn)品說明:
Low-warpage, easy-flowing injection molding grade with 10% glass fibres for technical parts, for which dimensional stability is very important (eg, housings, plug-and-socket connectors).
填料/增強(qiáng)材料 | 玻璃纖維增強(qiáng)材料, 10% 填料按重量
|
用途 | 工程配件、連接器外殼 |
機(jī)構(gòu)評(píng)級(jí) | |
RoHS 合規(guī)性 | |
外觀 | |
形式 | |
加工方法 | |
多點(diǎn)數(shù)據(jù) | Creep Modulus vs. Time (ISO 11403-1)Isochronous Stress vs. Strain (ISO 11403-1)Isothermal Stress vs. Strain (ISO 11403-1)Secant Modulus vs. Strain (ISO 11403-1)Shear Modulus vs. Temperature (ISO 11403-1)Viscosity vs. Shear Rate (ISO 11403-2) |
樹脂ID (ISO 1043) | |
密度 | 1.31 | g/cm3 | ISO 1183 |
表觀密度 | 0.70 到 0.80 | g/cm3 |
|
溶化體積流率（MVR） (275°C/2.16 kg) | 1.22 | in3/10min | ISO 1133 |
吸水率 |
|
| ISO 62 |
飽和, 73°F | 0.40 | % |
|
平衡, 73°F, 50% RH | 0.20 | % |
|
粘數(shù) 3 | 105 | cm3/g | ISO 307 |
模具收縮性 4 |
|
|
|
free, longitudinal | 0.46 | % |
|
free, transverse | 0.85 | % |
|
球壓硬度 (H 961/30) | 20300 | psi | ISO 2039-1 |
拉伸模量 | 653000 | psi | ISO 527-2 |
拉伸應(yīng)力 (斷裂) | 10900 | psi | ISO 527-2 |
拉伸應(yīng)變 (斷裂) | 2.9 | % | ISO 527-2 |
拉伸蠕變模量 5 (1000 hr) | 479000 | psi | ISO 899-1 |
彎曲模量 | 595000 | psi | ISO 178 |
彎曲應(yīng)力 | 17300 | psi | ISO 178 |
簡(jiǎn)支梁缺口沖擊強(qiáng)度 |
|
| ISO 179/1eA |
-22°F | 1.5 | ft·lb/in2 |
|
73°F | 1.9 | ft·lb/in2 |
|
簡(jiǎn)支梁無缺口沖擊強(qiáng)度 |
|
| ISO 179/1eU |
-22°F | 11 | ft·lb/in2 |
|
73°F | 18 | ft·lb/in2 |
|
熱變形溫度 |
|
|
|
66 psi, 未退火 | 374 | °F | ISO 75-2/B |
264 psi, 未退火 | 221 | °F | ISO 75-2/A |
熔融溫度 | 433 | °F | ISO 11357-3 |
線形熱膨脹系數(shù) - 流動(dòng) (73 到 176°F) | 3.1E-5 | in/in/°F | ISO 11359-2 |
比熱 | 0.287 | Btu/lb/°F |
|
導(dǎo)熱系數(shù) | 1.9 | Btu·in/hr/ft2/°F | DIN 52612 |
溫度指數(shù) - at 50% loss of tensile strength |
|
| IEC 60216 |
-- 6 | 230 | °F |
|
-- 7 | 284 | °F |
|
最高使用溫度 - short cycle operation | 338 | °F |
|
表面電阻率 | 1.0E+14 | ohms | IEC 60093 |
體積電阻率 | 1.0E+16 | ohms·cm | IEC 60093 |
相對(duì)電容率 |
|
| IEC 60250 |
100 Hz | 3.60 |
|
|
1 MHz | 3.40 |
|
|
耗散因數(shù) |
|
| IEC 60250 |
100 Hz | 3.1E-3 |
|
|
1 MHz | 0.021 |
|
|
漏電起痕指數(shù) |
|
| IEC 60112 |
解決方案 A | 375 | V |
|
解決方案 B | 125 | V |
|
可燃性等級(jí) |
|
| IEC 60695-11-10, -20 |
0.030 in | HB |
|
|
0.06 in | HB |
|
|
干燥溫度 | 176 到 248 | °F |
|
干燥時(shí)間 | 4.0 | hr |
|
建議的最大水分含量 | 0.040 | % |
|
料斗溫度 | 176 | °F |
|
料筒后部溫度 | 500 | °F |
|
料筒中部溫度 | 509 | °F |
|
料筒前部溫度 | 518 | °F |
|
射嘴溫度 | 518 | °F |
|
加工（熔體）溫度 | 482 到 527 | °F |
|
模具溫度 | 140 到 212 | °F |
|
Screw Speed | < 591 | in/min |
|
如需巴斯夫原廠物性表及相關(guān)文件，請(qǐng)聯(lián)系我們工作人員，謝謝！